Fiber for reinforcing plastic composites and reinforced plastic composites therefrom

ABSTRACT

A high tenacity fiber for reinforcing plastic composites, the fiber being selected from the group consisting of polyester, aliphatic polyamide, and combinations thereof. The fiber is treated with a composition consisting essentially of an organofunctional silane in an amount sufficient to achieve 0.02 to 1.0 weight percent of the silane on the fiber, and a diluent which provides for the hydrolysis of the silane to a silanol. The fiber is used to reinforce a plastic composite additionally comprising a resin matrix.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a high tenacity fiber for reinforcing plastic composites and to the composites themselves wherein the reinforcing fiber, selected from the group consisting of polyester, aliphatic polyamide and combinations thereof, has been treated with a composition consisting essentially of an organofunctional silane in an amount sufficient to achieve 0.02 to 1.0 weight percent of the silane on the fiber and a diluent which provides for the hydrolysis of the silane to a silanol. More particularly, the present invention relates to a high tenacity, high elongation, low shrinkage polyester fiber which has been treated with a composition consisting essentially of water and gamma-glycidoxypropyltrimethoxysilane in an amount sufficient to acheive 0.02 to 1.0 weight percent of the silane on the fiber, especially for use in reinforcing a composite wherein the resin matrix comprises unsaturated polyester resin or other thermosetting or thermoplastic resins. The reinforcements can be used in bulk and sheet molding compounds, filament winding, pultrusion, spray-up and hand-layup.

2. The Prior Art

A composite consists of basically three major elements: the resin matrix, the reinforcement dispersed in the matrix, and the reinforcement-resin matrix interface. Synthetic fibers in staple or filamentary form, and fabrics produced therefrom, are known for polymer reinforcement. Typical of the fibrous reinforcements are glass, polyester, polyamide (nylon and aramid) and polyolefin fibers. Conventional matrix resins include thermoplastics, such as nylon and polyolefins, and thermosetting materials, such as epoxy and unsaturated polyester resins. Since the primary function of the fiber matrix interface is to transmit stress from the matrix to the reinforcing fibers, the chemical and physical features of the interface are critical to the mechanical properties and end use performance of the composite. The compatibility between the reinforcing fiber and matrix is then a determining factor in the load sharing ability of the composite. Fiber coatings/binders have been used to enhance the compatability of the reinforcing fibers and resins with which they are to be used. See, for example, U.S. Pat. No. 3,637,417 to Green, hereby incorporated by reference. It is known to utilize silane coupling agents to bond dissimilar materials such as organic polymer and fibrous glass in the field of reinforced plastics. See, e.g., Green, supra, U.S. Pat. No. 4,158,714 to Brichta et al., and U.S. Pat. No. 3,658,748 to Andersen et al., and Marsden and Sterman, HANDBOOK OF ADHESIVES, Second Edition, 40, 640 (1977), all of which are hereby incorporated by reference. It is also known to utilize silane coupling agents to improve fiber to rubber adhesion, as taught by Japanese Kokai Publication No. J53-024423, hereby incorporated by reference, wherein a polyethylene terephthalate yarn is combined with from 0.7 to 1.2 weight percent on the yarn of a liquid composition consisting essentially of 10 to 30 weight percent of a silane having the structural formula ##STR1## wherein n is 2 to 5, up to one weight percent of a nonionic wetting agent and 70 to 90 weight percent water. The present invention, however, is directed towards reinforcement of plastic composites and not elastomeric structures.

It is also conventional to substitute organic synthetic fibers in whole or in part for glass fibers in reinforced plastics. Some advantages are pointed out in U.S. Pat. No. 3,639,424 to Gray et al., hereby incorporated by reference, wherein heatset polyester staple is used to reinforce thermoplastic/thermosetting polymers for improved impact strength. Heatsetting the fiber allegedly permits uniform fiber dispersion in molded products.

The use of chemically modified polyester fabric as an auxiliary reinforcing agent with glass fibers for thermosets, including polyester, vinyl ester and epoxy, for improved impact resistance and flexural strength over straight glass reinforcement is disclosed in Plastics World Magazine, November, 1980, Volume 38, No. 11, page 102, hereby incorporated by reference.

Japanese Kokai Publication No. 54-55077 discloses a method for adhesion of polyester fiber/fabric and unsaturated polyester resins through application of a latex, which preferably includes a small quantity of bisphenol epoxy resin, to the polyester fiber/fabric.

The present invention is directed towards improving compatability between a resin matrix and the reinforcing fibers to thereby enhance the reinforced composite properties.

SUMMARY OF THE INVENTION

The present invention provides a high tenacity reinforcing fiber selected from the group consisting of polyester, aliphatic polyamide and combinations thereof, for reinforcing composites. The fiber may be staple or continuous filament per se or a knitted, woven or nonwoven fabric or mats. The reinforcing fiber is treated with a composition consisting essentially of an organofunctional silane in an amount sufficient to achieve 0.02 to 1.0, preferably 0.1 to 0.5, weight percent of the silane on the fiber, and a diluent which provides for the hydrolysis of the silane to a silanol. Wettability of the fiber and adhesion of the fiber to a resin matrix are thereby enhanced, and the compatibility of such reinforcing fiber to the resin is improved so that composites with reinforcement uniformly dispersed therein can be fabricated.

It is preferred that the treating composition consist essentially of 1 to 50, preferably 3 to 25, weight percent of the silane; up to 1 weight percent of a wetting agent; and 49 to 99, preferably 74 to 97, weight percent of the diluent.

The preferred diluent is water although it is believed that aqueous systems containing other highly polar materials such as low molecular weight alcohols would be satisfactory. The preferred wetting agent is nonionic, e.g., polyoxyalkylene nonylphenols, octylphenoxyethanols, although anionic wetting agents such as the dialkylsulfosuccinates, particularly dinonyl and dioctyl), and 2-ethylhexylphosphate are suitable.

Organofunctional silane coupling agents may be found in chapter 40 of the HANDBOOK OF ADHESIVES, supra. The organofunctional silane utilized in the present invention is preferably selected from the group consisting of: Vinyl-tris(beta-methoxyethoxy) silane, gammaMethacryloxyalkyltrialkoxysilane, beta(3,4-Epoxycyclohexyl)alkyltrialkoxysilane, gamma-Mercaptoalkyltrialkoxysilane, gamma-Aminoalkyltrialkoxysilane, N-beta(aminoethyl)-gamna-aminoalkyltrialkoxysilane, and ##STR2## wherein n is 2 to 5, and combinations thereof. The most preferred silane is gamma-glycidoxypropyltrimethoxy silane.

The preferred reinforcing polyesters are the linear terephthalate polyesters, i.e., polyesters of a glycol containing from 2 to 20 carbon atoms and a dicarboxylic acid component containing at least about 75 percent terephthalic acid. The remainder, if any, of the dicarboxylic acid component may be any suitable dicarboxylic acid such as sebacic acid, adipic acid, isophthalic acid, sulfonyl-4,4'-dibenzoic acid, 2,8-dibenzofuran-dicarboxylic acid, or 2,6-naphthalene dicarboxylic acid. The glycols may contain more than two carbon atoms in the chain, e.g., diethylene glycol, butylene glycol, decamethylene glycol, and bis-(1,4-hydroxymethyl)cyclohexane. Examples of linear terephthalate polyesters which may be employed include poly(ethylene terephthalate), poly(ethylene terephthalate/ 5-chloroisophthalate)(85/15), poly(ethylene terephthalate/5-[sodium sulfo]-isophthalate) (97/3), poly(cyclohexane-1,4-dimethylene terephthalate), and poly(cyclohexane-1,4-dimethylene terephthalate/hexahydroterephthalate) (75/25).

Suitable reinforcing polyamides include, for example, those prepared by condensation of hexamethylene diamine and adipic acid, condensation of hexamethylene diamine and sebacic acid known as nylon 6,6 and nylon 6,10, respectively, condensation of bis(para-aminocyclohexyl)methane and dodacanedioic acid, or by polymerization of 6-caprolactam, 7-aminoheptanoic acid, 8-caprylactam, 9-aminopelargonic acid, 11-aminoundecanoic acid, and 12-dodecalactam, known as nylon 6, nylon 7, nylon 8, nylon 9, nylon 11, and nylon 12, respectively.

The most preferred reinforcing fiber is a polyethylene terephthalate, characterized by a thermal shrinkage of up to about 11 percent, preferably 3 percent or less; an elongation of from about 10 to 28, preferably 14 to 24 percent; a modulus after cure of at least about 60, preferably 70 to 90 grams per denier; and a tenacity of at least 5.5, preferably 7 to 9 grams per denier. By modulus after cure is meant the modulus of the fiber after exposure in an unconstrained state to curing temperatures for the composite.

The present invention also relates to a fiber reinforced plastic composite comprising a resin matrix and the described reinforcing fiber.

The resin matrix may include thermosetting or thermoplastic (including polyolefin) resins. Suitable thermosetting resins include polyester (preferably unsaturated), epoxy, or vinyl ester resin systems. Suitable thermoplastic resin systems include polyvinyl chloride, polyethylene, polypropylene, polystyrene, polyvinyl alcohol, polyamide, polyurethane, etc.--any thermoplastic having a lower melting point than that of the fiber, e.g., less than 230° C. for reinforcement with polyester fibers and less than 200° C. for reinforcement with nylon fibers.

The resin matrix also may include enhancers, mold release agents and fillers, as are known in the composite art, in addition to the treated fibers and resins.

It is also preferred that there be other reinforcing fibers, more preferably glass fibers, as will be more fully discussed below.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph depicting the effect of thermal exposure on (a) shrinkage and (b) fiber modulus;

FIG. 2 is a graph depicting the effect of fiber length and loading on composite properties;

FIG. 3 schematically shows the equipment utilized to evaluate interfacial shear strength;

FIG. 4 is a graph depicting the effect of interfacial shear strength on composite properties;

FIG. 5 is a photograph of an adhesion test sample;

FIG. 6 is a graph depicting the effect of fiber loading on composite properties; and

FIGS. 7A-D are bar graphs of BMC injection molded composite properties.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Preliminary research was directed towards engineering a polyethylene terephthalate (hereafter PET) fiber specifically for reinforcement of rigid composites. Research first addressed the question of what type of PET fiber is most suitable as a reinforcing fiber in composites. There are many grades of PET commercially available. However, preliminary screening showed only very specific types to be even potentially useful in composites.

With reference to Table I, it can be seen that textile grade PET fiber (Burnet Southern, Inc.) is unsuitable for reinforcement, primarily because of its low tenacity, low modulus, and large thermal shrinkage, resulting in a composite with poor notched impact strength.

It was expected that high tenacity industrial PET fibers could provide superior impact strength with adequate tensile strength. Preliminary work showed this to be true; however, a wide range of values was obtained based on differing fiber types. It has been found that tensile properties of the fiber as normally measured, as well as after exposure to the thermal molding conditions encountered in fabricating a reinforced composite article, are important. The latter is more important since the final properties of the fiber in the composite more directly affect composite performance.

EXAMPLE 1

Data for three types of high strength industrial PET fibers, commercially available from Allied Corporation, are shown in Table 1. These are: Type A--a high tenacity, low elongation fiber normally used for tire reinforcement; Type B--a high tenacity, high elongation, low shrinkage fiber normally used for hose reinforcement; and Type C--a high tenacity, high elongation, ultralow shrinkage fiber normally used for coated fabrics. Molded composite specimens were prepared from each of the fibers using a 12 weight percent PET fiber loading, equivalent in volume to 20 weight percent glass. The type B fiber appeared to give the best balance of composite properties. This is unexpected based on initial fiber properties.

The fibers were subjected to simulated curing temperatures of from 95°-150° C. while in an unconstrained state. Fiber physical properties were measured both before (control) and after heat treatment. The effects of thermal exposure on Fibers A, B and C, respectively are presented in Tables 2-4.

As shown in FIG. 1-a, Type A underwent a large amount of shrinkage at temperatures as low as 120° C. In contrast, the two low shrinkage fibers B and C showed very little shrinkage during thermal exposure, as expected. Since excessive shrinkage during processing would have a detrimental effect on fiber/resin bonding, this might be expected to result in reduced composite properties.

The thermal exposure also had greatly differing effects on the moduli of the different fibers tested (reference FIG. 1-b). When tested at room temperature, the high tenacity Type A fiber had a 20-25 percent higher initial modulus and 10 percent higher tenacity than the low shrink fibers. However, after exposure to the elevated temperatures, the Type A fiber showed a more dramatic change than either of the others. Also, and not to be expected from normal measured physical properties, the final modulus of Type A was nearly 30 percent lower than the final modulus of the two low shrink fibers after exposure to 150° C. Therefore, in their effect on composite properties, the two low shrinkage fibers appear to be superior in spite of the fact that tensile properties on virgin yarn appear to be superior for the Type A fiber.

The ultralow shrink Type C fibers tested had a lower molecular weight, which results in a lower tensile strength fiber than the Type B low shrink fiber. It was found that the initial tenacity was essentially unchanged by thermal treatment for any of the fibers. Therefore, the slightly better dimensional stability of the Type C ultra low shrink fiber is more than offset by the higher tenacity Type B low shrink fiber.

                  TABLE 1                                                          ______________________________________                                         Fiber and Composite Properties.sup.1                                           ______________________________________                                                Fiber Properties                                                                                             Thermal                                            Tenacity.sup.4                                                                           Modulus.sup.5                                                                            Elonga- Shrink-                                   Fiber    gpd       gpd       tion, %.sup.6                                                                          age, %.sup.7                              ______________________________________                                         E-Glass  6.5       320       2.1     0                                         Textile Fiber.sup.2                                                                     4.5       30-40     30      5-8                                       Type A.sup.3                                                                            8.9       123       14      9.1                                       Type B.sup.3                                                                            8.1        98       22      1.8                                       Type C.sup.3                                                                            7.6        99       21      0.6                                       ______________________________________                                                 Composite.sup.1 Properties                                                       Notched      Tensile                                                           Impact       Strength Flexural                                       Fiber     ft lb/in.sup.8                                                                              psi.sup.9                                                                               psi.sup.10                                     ______________________________________                                         E-Glass   4.4          5000     15 200                                         Textile Fiber.sup.2                                                                      2.9          2900     2500                                           Type A.sup.3                                                                             8.4          2500     4100                                           Type B.sup.3                                                                             9.7          2900     4300                                           Type C.sup.3                                                                             9.4          2700     4400                                           ______________________________________                                          .sup.1 Polyester BMC formulation                                               20 weight percent glass, glass replaced by PET on equal volume basis           Fiber length = 0.25 inch (0.64 cm)                                             Balance 18.33% isophthalic polyester resin (MR 14017 USS Chemicals), 5.86      resinous modifier (MR 63004 USS Chemicals), 0.31% tertbutyl(perbenzoate),      0.12% promoter, 0.01% inhibitor solution (butylated hydroxy toluene and        styrene), 1.30% zinc stearate, 52.5% aluminum trihydrate, 1.50% pigment        (CM7106 Red by Plastic Colors).                                                .sup.2 Commercially available from Burnet Southern.                            .sup.3 Commercially available from Allied Corporation.                         .sup.4 ASTM D885.                                                              .sup.5 ASTM D885.                                                              .sup.6 ASTM D885.                                                              .sup.7 ASTM D885.                                                              .sup.8 ASTM D256                                                               .sup.9 ASTM D638.                                                              .sup.10 ASTM D790                                                        

The optimum PET fiber length for staple reinforcement appears to be the longest length which will still allow practical handling and dispersion. Notched impact strength showed a significant response to fiber length. Three fiber lengths, 1/8, 1/4 and 1/2 inch (0.32, 0.64 and 1.3 cm) were used to determine the affect of PET fiber length at several levels of total fiber loading. Results are plotted in FIGS. 2a and b. For each doubling of fiber length the impact strength also doubled. Subsequent testing showed that a 3/4 inch (1.9 cm) PET fiber reinforced composite resulted in still more improved impact strength. There was little difference in composite tensile strength between 1/8 and 1/4 inch (0.32 and 0.64 cm) fiber. However, using 1/2 inch (1.3 cm) fiber resulted in an increase in tensile strength of about 50 percent. These results point out a significant advantage of an organic filament reinforcement. In contrast to glass, which can shatter into shorter lengths during compounding, PET fiber does not break into shorter lengths. This allows PET fiber to retain its maximum advantage for impact strength.

EXAMPLE 2

It is known that the fiber coating is a factor in stress distribution for the composite. In preliminary studies it was observed by scanning electron microscope that a very nonuniform wetout and poor adhesion were achieved between PET fibers and thermoset polyester resins. To improve these features for thermoset polyester resins various types of fiber coatings were used. The properties of these coatings were varied in order to determine the degree of influence of the boundary on the composite performance.

The binders applied are listed in Table 5. The yarn utilized was Type B of Table 1. Yarn was removed from a supply package at 1000 ft/min (305 m/min) and passed over a stainless steel lube roll that was partially immersed in the binder/finish composition, after which the yarn was passed through drive rolls and thence to a winder where it was wound. The yarn was removed from the supply package through eyelet guides and two tension gates to flatten the yarn bundle for passage over the roll and to prevent bouncing. The yarn touched the roll as a tangent, a minimum contact angle being maintained. The lube roll was 4 inches (10 cm) in diameter and turning at an RPM sufficient to achieve the percent solids on yarn indicated in Table 5. For the composition of the present invention, the roll was turning at 15 RPM.

Several methods to determine the adhesive properties of the PET fiber were evaluated. For comparison and evaluation purposes, the adhesive properties were measured as a function of the interfacial shear strength. The interfacial shear strength was calculated from the pullout load, P using the following equation

    τ=P/DπL

where

τ=interfacial shear strength,

D=fiber diameter, and

L=embedded fiber length in the matrix.

A small portion of an overfinished PET fiber was embedded to a depth of 0.25 inch (0.64 cm) in a compounded thermoset polyester resin of the formulation set forth in Table 1. FIG. 3 depicts the setup for the operation utilized to evaluate the interfacial shear strength. The fiber 11 was subjected to a tensile force (pullout force) with an Instron 12 in the axial direction of the filaments, causing shear debonding stress on the interface. The Instron 12 has a recorder 13 attached thereto to record the pullout load, P, in pounds (kg). By using this technique, the effect of use of different binders on the interfacial strength of the composite could be determined. This test is called the button mold pullout test. The interfacial shear strength is the total overall strength of the interface due to physical, mechanical and chemical bonding. The composite physical properties were determined for the different interfacial shear strength values delivered by the different binders, to a level of about 7.3 kg/cm², composite properties improved proportional to τ; however, at just over 7.3 kg/cm² data seem to show that maximum composite properties were achieved and further increases in interfacial shear strength were detrimental. In fact, what was observed is that the type of materials which achieve a high concentration of crosslinking sites and therefore a very high interfacial shear strength showed a poor wetout by the resin. This poor resin wetout created a number of voids and flaws which acted as stress concentrators within the matrix leading to early failure. Thus, fiber/matrix wettability is also a key to better load sharing and transferring between phases.

The wettability of the treated fibers listed in Table 5 by the specified resin was determined as follows. A value of 1 to 10 was assigned to a particular fiber wherein 1=poor and 10=excellent based on visual inspection and two tests. The visual examination occurred during BMC compounding of 1/2 inch (1.3 cm) length PET filament (1000 denier, 192 filaments) at 20 percent loading (i.e., volume equivalent 20 weight percent fiberglass) with the resin matrix set forth before. The resin matrix included 1.5 weight percent of a red pigment available as CM-7106 from Plastic Colors to aid the visual inspection. After compounding for 60 seconds, the compounded mass was manually pulled apart, fibers pulled out and felt for wetness and observed for color change. Compounding was restarted and continued for 30 seconds after which the same observations were made. This continued until maximum wetout of the fiber occurred. For fibers with binder systems 2 and 5 (Table 5) the visual inspection also included examination of the fiber bundle for spreadability and pickup of the resin during a filament winding process when the fiber bundles were run in parallel and with minimal tension under a roll in a resin bath; the resin was a polyester resin (50 parts Freeman 40-2092 and 52 parts Freeman 40-2490). Fiber with binder system 5 had a vastly greater pickup than fiber with binder system 2. One of the tests relied upon in forming the wettability value was using a scanning electron microscope (SEM) to evaluate broken composites. The fibers of Table 5 were used to compound a 20 percent load PET fiber reinforced BMC compound. These compounds were molded [320° F. (160° C.), 1.5 min, 1 ton press] into tensile, flexural and impact specimens, as well as plaques. The specimens were broken for testing in accordance with ASTM tests: the tensile specimen according to D-638, the flexural according to ASTM D-790 and the impact specimen according to ASTM D-256. The plaques were manually broken. The broken specimens and plaques were taken to an SEM laboratory for examination. The fibers jutting out from the fracture point were observed for residual matrix or matrix cling. If the fiber was clean, adhesion and wetout were ranked 1. The more matrix clinging to the fiber, the higher the ranking, up to a rating of 10. Button test specimens could be similarly evaluated. SEM photographs, the button sample and the pulled out fiber are shown in FIG. 5. FIG. 5-a shows the section of the fiber that was embedded where pieces of the matrix cling to the fiber. FIG. 5-b shows the orifice from which the fiber was pulled. SEM rankings are presented in Table 6. In another test the contact angle of a polyester molding resin (MR14017 from USS Chemicals) on a unidirectional fabric made with the coated yarns was measured. The unidirectional fabric was made by guiding the coated PET fiber bundles over a winding mechanism so that a fabric could be made from closely packed parallel fiber bundles. A sessile drop of the liquid molding resin was placed on the fabric held under tension (0.2 gram/fil), and the contact angle on the fabric was measured with time. The contact angles measured are presented in Table 6 as well as a ranking of the coated fibers with respect to wettability.

PET fiber inherently has low fiber bundle integrity (fiber bundle integrity is the degree to which the individual filaments adhere to each other). The main benefit of a low integrity fiber is that it allows the dispersion of single filaments over a large resin matrix area. This even distribution results in a homogeneous reinforced composite, a direct result of which is an improved cosmetic look.

The binder system of the present invention (number 5 of Table 5) was chosen as the low integrity system because of its good adhesion and exceptional resin wetout. This was despite the fact that fiber with binder system 2 resulted in a composite with equal or better physical properties. See Table 7. Note that the major difference between binder systems 2 and 5 is the additional oils in the noncontinuous phase for system 2, i.e., both systems include the same epoxy silane and water. However, these benefits could not offset the exceptional resin wetout of the fiber with binder system 5 during processing, as observed during filament winding operations. This increase in wettability was also seen in BMC processing in the form of improved mixing and surface appearance. In addition, the BMC composite physical properties for the fiber with binder system 5 were acceptable. The binder wettability characteristics were also measured via contact angle and again, fiber with binder system 5 showed a major edge over the balance of the system. Fiber with binder system 2, when used in forming a BMC plaque, evidenced white, dry spots of yarn in the plaque, which were aesthetically unacceptable. This is critical, given the market for such composites.

EXAMPLE 3

Several thermoset polyester resins were evaluated to determine the best for composite applications where 0.5 inch (1.3 cm) PET fiber coated with 0.2 weight percent solids of binder system 2 was used as reinforcing fiber, alone and in combination with glass. A sample with 100 percent glass reinforcement was also run. Total fiber loading was kept constant at the volume equivalent to 20 weight percent glass. The curing temperature used was 300° F. (149° C.). Typical composite physical properties were measured on the molded samples, and are shown in Table 8. Resin matrix formulation was as previously described, with the resins identified in Table 8.

Impact strength is a measure of a composite's resistance to a sudden sharp impact. Replacement of glass fiber by polyester fiber results in a great improvement in this property. Two types of impact tests were run, notched and unnotched. In the notched impact test, impact strength for 100 percent PET fiber reinforced composite increased from 15 to 20 foot pound/inch as the resin elongation was increased from 0.9 percent to 10 percent. For the 100 percent glass reinforced composite and composites reinforced by mixtures of PET fibers and fiberglass, impact strength remained relatively constant with increasing resin elongation. As the proportion of PET fiber was increased, the impact strength was seen to increase at all resin elongations. The increase was greater at the higher resin elongations. Results of the unnotched impact test showed the same general trends observed in the notched test. In this case, however, the composites were reinforced by 100 percent glass fibers, and PET/glass fiber mixtures tended to lose impact strength as resin elongation increased. Again, as the proportion of PET fiber and the reinforcing fiber increased, impact strength increased at all resin elongations with the increase being larger at higher elongations. These results demonstrate that higher elongation resins are preferable for increased impact strength for PET fiber reinforced composites.

While PET is stronger than glass on a strength per unit weight basis (9.0 gpd versus 6-8 gpd), the fact that a specific gravity is nearly 50 percent lower than glass means that an equivalent volume of PET fibers will be less strong than glass fibers. Thus, PET reinforcing fibers provide a molded part which is not as strong as that reinforced by 100 percent glass fibers.

On an equal volume loading basis, composite strength decreased roughly by a factor of 2 going from 100 percent glass fiber reinforced composite to a 100 percent PET fiber reinforced composite. The change in tensile strength with PET/glass fiber ratio showed a linear relationship in all resin systems, indicating that composite strength followed the rule of mixtures well.

Tensile strength did not change dramatically with resin elongation. In general, the maximum value occurred using the 6.1 percent elongation resin, with the tensile strength being 10 to 25 percent higher than for the high and low elongation resin. The PET/glass ratio of the reinforcing fiber used did not appreciably affect the location of this maximum. Therefore, the 6.1 percent elongation resin appears to be the resin of choice to maximize the tensile strength of PET reinforced composites.

Flexural strength is another measure of the strength of a composite material, having both tensile and compressive components. The same general trends were seen here that were noted for tensile strength. For 100 percent PET fiber and 100 percent glass fiber reinforced composites the maximum tensile strength was obtained using the 6.1 percent elongation resin. This was also the case for the sample reinforced by a 12.5/87.5 PET/glass fiber mixture. The samples reinforced by 25/75 and 50/50 PET/glass fiber mixtures showed a steady increase in flexural strength with increasing resin elongation. Flexural strength gains of 10 to 30 percent were obtained by using the 6 or 10 percent elongation resins relative to the 0.9 percent elongation resin typically used with 100 percent fiberglass reinforced composites. Therefore, the use of a medium to high elongation resin is preferable to maximize flexural strength.

With the exception of Barcol hardness, increasing the resin elongation over that typically used (0.9%) with glass fiber resulted in improved composite physical properties. Tensile and flexural strength had the maximum values using a resin with a 6.1 percent elongation to break. This medium elongation resin thus appeared to be the best for use with the PET fiber coated with a binder system.

EXAMPLE 4

As generally recognized, the mechanical properties of a reinforced composite are strongly dependent on the level of reinforcing fiber used. In general, the properties improve with total fiber loading up to a maximum loading where the mechanical properties level or fall off due to inadequate fiber dispersion or insufficient resin to form a good matrix.

In this example BMC formulations were made using 100 percent of PET fiber coated with binder system 2, 100 percent glass fiber, and mixtures of the PET fiber and glass fiber as the reinforcing agent. Fiber loadings were reported as the weight percent glass equivalent to the total fiber volume loading used. Total fiber loadings of 10 to 35 percent were used. Sample specimens were made and tested for tensile strength and impact strength. See Table 9.

With each reinforcing system the impact strength increased with increasing fiber loading, as shown in FIG. 6. The best impact strengths were seen for the composites reinforced with 100 percent PET fiber, having values as high as 21 foot pound/inch. Impact strengths for the PET/glass fiber mixtures were in between the values for the 100 percent PET reinforced composites and the 100 percent glass fiber reinforced composites.

For this BMC formulation, total fiber loading equivalent to about 25 percent by weight fiberglass appeared to be optimum. Beyond this level, difficulties began to be encountered in compounding, while only small additional gains in impact strength were seen.

Tensile strengths also increased with increasing total fiber loading for each of the reinforcing systems studied and as shown in FIG. 6. PET fiber is as strong as glass fiber on a weight basis, but because of the higher density of glass, glass reinforced composites are stronger on an equal volume reinforcement basis. However, at the 20-25 percent loading level, the composites reinforced by PET/glass fiber mixtures were nearly as strong as the 100 percent glass reinforced composites.

EXAMPLE 5

In this example bulk molding compounds containing 20 weight percent glass loading, glass replaced by PET fiber on equal volume basis, were made and molded into specimens for testing. The BMC resin matrix was as previously described, and the PET fiber had been treated with binder system 2. The composition of the reinforcing fibers was varied, with relative polyester fiber/glass fiber volume ratios of 0/100, 25/75, 50/50, and 100/0 being used. All fiber loading levels reported are given as the weight percent glass equivalent to the particular volume of loading of the fiber used. The same composite properties were measured as reported previously and the results are given in Table 10. These data show that partial replacement of glass fiber by PET fiber in a reinforced composite results in significant gains in impact strength with very little sacrifice in tensile strength, especially at a fiber ratio of 25/75 PET/glass. This results in molded parts with overall properties which are superior to parts reinforced by either fiber used alone.

Studies were also run on BMC injection molded composites reinforced by all PET fiber, all glass fiber, and PET/glass fiber mixtures to determine the effect. The results are presented in Table 11 and shown graphically in FIGS. 7A-D.

The replacement of glass fibers by PET fibers resulted in greater increases in impact strength than were observed for compression molded samples. At the same time, tensile strength and flexural strength were less effective by replacement of glass with PET fibers than in compression molded samples. This is presumably due to the fact that shear and the injection molding machine broke the glass fibers into shorter lengths without affecting the lengths of the PET fibers. In addition, it may be possible that the presence of the PET fibers protect the glass fibers from damage to some extent.

EXAMPLE 6

Binder systems are formulated similar to that of system 5, but substituting the following organofunctional silanes for the silane of system 5:

Vinyl-tris(beta-methoxyethoxy)silane;

gamma-Methacryloxyalkyltrialkoxysilane;

beta(3,4-Epoxycyclohexyl)alkyltrialkoxysilane;

gamma-Mercaptoalkyltrialkoxysilane;

gamma-Aminoalkyltrialkoxysilane; and

N-beta(aminoethyl)-gamma-aminoalkyltrialkoxysilane.

These systems are used to overfinish type B (Table 1) PET fibers for reinforcement of plastic composites. Performance should be comparable to PET fiber treated with binder system 5.

EXAMPLES 7-8

PET fiber type B with binder system 5 at 0.20% solids pickup was cut into 3/4 and 1 inch (1.9 and 2.5 cm) lengths in Examples 7 and 8, respectively, and used to compound a 20 percent load, 100 percent PET fiber reinforced BMC compression compound with the resin matrix formulation of Table 1 (6.1% elongation resin). Excellent composite properties were obtained.

EXAMPLE 9

Nylon 6 fiber having a nominal denier of 1260, 204 filaments, modulus of 44, breaking strength (lbs) 24.5, tenacity 8.8 gpd, breaking elongation (%) 20.5, commercially available from Allied Corporation, had binder system 5 applied via a kiss roll at a solids pickup of 0.20 percent. The fiber was cut into 0.5 inch (1.3 cm) lengths and used to compound a 20 percent load nylon reinforced BMC compression composite with the resin matrix formulaton of Table 1. Composite properties are presented in Table 11.

                  TABLE 2                                                          ______________________________________                                         Effect of Thermal Exposure on Fiber A                                                         Thermal          Elonga-                                        Exposure                                                                               Time   Shrinkage,                                                                               Tenacity,                                                                             tion    Modulus                                Temp. °C.                                                                       Min.   percent   gpd    Percent gpd                                    ______________________________________                                         --*     --     9.1       8.8    13.1    123.2                                   95     1      8.8       9.0    13.2    114.9                                   95     3      8.5       9.3    13.7    112.8                                   95     10     9.2       8.8    14.0    105.2                                   95     20     8.4       9.1    14.6    106.6                                  120     1      5.6       9.3    18.6    95.6                                   120     3      6.0       9.2    19.5    85.2                                   120     10     4.8       9.2    20.4    85.9                                   120     20     4.4       9.0    20.2    82.4                                   150     1      1.1       8.7    26.1    62.4                                   150     3      0.2       8.6    28.2    63.8                                   150     10     0.6       9.0    27.6    65.2                                   150     20     0.2       8.9    28.8    62.4                                   ______________________________________                                          *Control                                                                 

                  TABLE 3                                                          ______________________________________                                         Effect of Thermal Exposure on Fiber B                                                         Thermal          Elonga-                                        Exposure                                                                               Time   Shrinkage,                                                                               Tenacity,                                                                             tion    Modulus                                Temp. °C.                                                                       Min.   percent   gpd    Percent gpd                                    ______________________________________                                         --*     --     1.8       8.1    22.1    97.8                                    95     1      1.5       8.0    21.7    91.2                                    95     3      1.4       8.1    22.0    92.2                                    95     10     1.6       7.9    20.9    93.6                                    95     20     1.3       7.9    21.6    89.8                                   120     1      1.1       7.9    22.0    88.1                                   120     3      1.0       8.0    22.2    88.4                                   120     10     0.9       7.9    22.6    86.3                                   120     20     0.9       7.9    22.4    86.3                                   150     1      0.3       7.8    23.6    84.6                                   150     3      0.0       7.9    24.9    77.8                                   150     10     0.1       7.7    23.8    81.1                                   150     20     0.0       7.9    25.4    76.6                                   ______________________________________                                          *Control                                                                 

                  TABLE 4                                                          ______________________________________                                         Effect of Thermal Exposure on Fiber C                                                         Thermal          Elonga-                                        Exposure                                                                               Time   Shrinkage,                                                                               Tenacity,                                                                             tion    Modulus                                Temp. °C.                                                                       Min.   percent   gpd    Percent gpd                                    ______________________________________                                         --*     --     0.6       7.6    20.7    99.1                                    95     1      0.3       7.1    20.5    91.5                                    95     3      0.2       7.2    20.9    91.5                                    95     10     0.3       7.4    21.0    90.1                                    95     20     0.1       7.5    21.1    89.4                                   120     1      0.0       7.6    22.0    90.8                                   120     3      0.0       7.5    21.6    92.2                                   120     10     0.0       7.5    21.9    88.0                                   120     20     0.0       7.0    21.1    86.0                                   150     1      0.0       7.1    21.0    88.0                                   150     3      0.0       7.2    22.2    86.0                                   150     10     0.0       7.5    23.2    86.7                                   150     20     0.0       7.1    22.4    88.7                                   ______________________________________                                          *Control                                                                 

                  TABLE 5                                                          ______________________________________                                         Treated Polyester (PET) Fiber Properties                                       ______________________________________                                         Binder     % Solids  Breaking   Breaking                                       System     Pickup    Strength (kg)                                                                             Elongation (%)                                 ______________________________________                                         1 (control)                                                                               --        7.66       21.4                                           2.sup.1 (comparative)                                                                     1.1       8.48       21.8                                           3.sup.2 (comparative)                                                                     0.28      --         --                                             4.sup.3 (comparative)                                                                     0.15      7.80       20.3                                           5.sup.4    0.20      8.07       20.0                                           6.sup.5 (comparative)                                                                     0.18      8.16       21.5                                           7.sup.6 (comparative)                                                                     0.44      7.98       19.0                                           8.sup.7 (comparative)                                                                     0.37      7.80       19.9                                           9.sup.8 (comparative)                                                                     0.45      8.03       19.7                                           ______________________________________                                                                      Interfacial                                                                    Shear                                             Binder     Tenacity Modulus  Strength                                                                               Wetta-                                    System     (gpd)    (gpd)    (kg/cm.sup.2)                                                                          bility                                    ______________________________________                                         1 (control)                                                                               7.7      88.5     6.67    5.0                                       2.sup.1 (comparative)                                                                     8.2      97.3     7.20    4.0                                       3.sup.2 (comparative)                                                                     --       --       7.10    8.5                                       4.sup.3 (comparative)                                                                     7.8      98.2     7.49    3.0                                       5.sup.4    8.1      98.9     7.30    8.5                                       6.sup.5 (comparative)                                                                     8.2      94.0     7.06    6.0                                       7.sup.6 (comparative)                                                                     8.0      88.5     7.57    6.5                                       8.sup.7 (comparative)                                                                     7.8      88.8     --      4.0                                       9.sup.8 (comparative)                                                                     8.0      87.8     --      4.0                                       ______________________________________                                          .sup.1 Gammaglycidoxypropyltrimethoxysilane, water and oil (3.6, 67.5 and      28.9%); oil phase included (isohexadecylstearate, glycerol monooleate,         decaglycerol tetraoleate, POE(15) tall oil fatty acid, sulfonated glycero      trioleate, and POE(20) tallow amine (approximately 62.7, 5.9, 7.9, 7.8,        11.8 and 3.9%).                                                                .sup.2 Vinyl chloride copolymer.                                               .sup.3 Saturated polyester resin.                                              .sup.4 Gammaglycidoxypropyltrimethoxysilane, POE(9-10) octylphenol and         water (84.9, 0.1 and 15 percent, respectively).                                .sup.5 Isophthalic acid, trimellitic anhydride and diethylene glycol resi      in water.                                                                      .sup.6 Trimellitic anhydride and propylene glycol resin in water.              .sup.7 Unsaturated polyester resin in water.                                   .sup.8 Unsaturated polyester resin.                                      

                  TABLE 6                                                          ______________________________________                                         Wettability                                                                    Binder        Contact   Ranking Aesthetic                                                                             Wettability                             System*                                                                               SEM    Angle (°'s)                                                                       1    2**  Rating Index                                 ______________________________________                                         1      5      54        --   --   5      5.0                                   2      5      59        --   --   3      4.0                                   3      8      45        4    1    9      8.5                                   4      3        81***   --   5    3      3.0                                   5      8      41        1    2    9      8.5                                   6      6      50        3    4    6      6.0                                   7      6      66        2    3    7      6.5                                   8      4      71        --   --   4      4.0                                   9      4      69        5    --   4      4.0                                   ______________________________________                                         *See Table 1 for details.                                                      **External evaluation of fibers with the five binder                           systems set forth wherein yarn was removed from a creel,                       passed through an isophthalic polyester resin (as in                           filament winding) bath under a roll partially submerged                        therein, passed through a slot stripper (to remove                             excess resin) and wound circumferentially on a flat                            mandrel. Tension was 5 pounds on each fiber.                                   Observations were as follows:                                                  Binder System                                                                  3   Fiber tended to fuzz before and                                                after resin bath. The fiber                                                    appeared to wet out almost                                                     immediately in bath.                                                       5   No fuzz noted. Wet out almost as                                               fast as 3.                                                                 4   No fuzzing noted when winding. The                                             fiber did not wet initially and                                                after winding the fibers still                                                 appeared only partially wet out.                                           6   No fuzz noted. Appeared slightly                                               better than Binder 7. After wound,                                             appeared like 3.                                                           7   No fuzzing noted. Took a couple of                                             minutes to soak in. Wetted better                                              than Binder 5. After wound, appeared                                           like 3.                                                                    ***Slightly modified formulation appears to give much                          better contact angle, i.e., about 40-50°.                          

                  TABLE 7                                                          ______________________________________                                         BMC Composite Properties for Fibers                                            ______________________________________                                                     Fiber Ratio  % Solids Barcol                                       Binder System.sup.1                                                                        PET/Glass    Pickup   Hardness                                     ______________________________________                                         1 Control   100/0        --       34.8                                         2 Comparative                                                                              100/0        1.1      42.6                                         3 Comparative                                                                              100/0        0.28     37.7                                         4 Comparative                                                                              100/0        0.15     39.5                                         5 Invention 100/0        0.20     41.2                                         6 Comparative                                                                              100/0        0.18     37.0                                         7 Comparative                                                                              100/0        0.15     37.4                                         8 Comparative                                                                              100/0        0.12     36.7                                         9 Comparative                                                                              100/0        0.15     37.2                                         10.sup.2 Comparative                                                                         0/100      --       47.1                                         11.sup.3 Comparative                                                                        0/0         --       42.2                                         ______________________________________                                                             Impact Strength                                                      Shrinkage (ft lbs/in)                                                Binder System.sup.1                                                                        (inches)    Notched  Unnotched                                     ______________________________________                                         1 Control   0.0099      18.28    25.21                                         2 Comparative                                                                              0.0055      16.86    25.96                                         3 Comparative                                                                              0.0103      17.32    25.05                                         4 Comparative                                                                              0.0098      16.52    23.28                                         5 Invention 0.0079      15.72    23.00                                         6 Comparative                                                                              0.0102      16.87    22.21                                         7 Comparative                                                                              0.0106      17.75    25.45                                         8 Comparative                                                                              0.0076      16.64    25.70                                         9 Comparative                                                                              0.0078      15.78    21.28                                         10.sup.2 Comparative                                                                       0.0003       8.81    11.18                                         11.sup.3 Comparative                                                                       0.0080       0.19     0.87                                         ______________________________________                                                      Flexural Strength                                                                           Tensile Strength                                     Binder System.sup.1                                                                         (PSI × 100)                                                                           (PSI × 100)                                    ______________________________________                                         1 Control    6.22         3.31                                                 2 Comparative                                                                               5.52         3.45                                                 3 Comparative                                                                               5.46         3.57                                                 4 Comparative                                                                               6.35         3.30                                                 5 Invention  6.24         3.50                                                 6 Comparative                                                                               5.52         3.54                                                 7 Comparative                                                                               5.32         3.49                                                 8 Comparative                                                                               5.22         3.10                                                 9 Comparative                                                                               5.15         3.45                                                 10.sup.2 Comparative                                                                        13.17        8.63                                                 11.sup.3 Comparative                                                                        2.60         0.95                                                 ______________________________________                                                     Fiber Ratio  % Solids Barcol                                       Binder System.sup.1                                                                        PET/Glass    Pickup   Hardness                                     ______________________________________                                         1 Control   50/50        --       43.3                                         2 Comparative.sup.4                                                                        50/50        1.1      47.0                                         3 Comparative                                                                              50/50        0.28     45.7                                         4 Comparative                                                                              50/50        0.15     42.5                                         5 Invention 50/50        0.20     41.5                                         6 Comparative                                                                              50/50        0.18     43.8                                         7 Comparative                                                                              50/50        0.15     45.1                                         8 Comparative                                                                              50/50        0.12     41.8                                         9 Comparative                                                                              50/50        0.15     43.3                                         10.sup.2 Comparative                                                                        0/100       --       47.1                                         11.sup.3 Comparative                                                                       0/0          --       42.2                                         ______________________________________                                                             Impact Strength                                                      Shrinkage (ft lbs/in)                                                Binder System.sup.1                                                                        (inches)    Notched  Unnotched                                     ______________________________________                                         1 Control   0.0011      12.45    17.94                                         2 Comparative                                                                              0.0016      11.64    17.21                                         3 Comparative                                                                              0.0013      12.96    18.28                                         4 Comparative                                                                              0.0011      12.49    20.62                                         5 Invention 0.0013      12.63    19.07                                         6 Comparative                                                                              0.0010      13.12    20.68                                         7 Comparative                                                                              0.0090      11.97    16.17                                         8 Comparative                                                                              0.0014      10.86    19.12                                         9 Comparative                                                                              0.0013      11.46    16.35                                         10.sup.2 Comparative                                                                       0.0003       8.81    11.18                                         11.sup. 3 Comparative                                                                      0.0080       0.19     0.87                                         ______________________________________                                                      Flexural Strength                                                                           Tensile Strength                                     Binder System.sup.1                                                                         (PSI × 100)                                                                           (PSI × 100)                                    ______________________________________                                         1 Control    10.17        5.47                                                 2 Comparative                                                                               8.84         5.41                                                 3 Comparative                                                                               10.53        4.84                                                 4 Comparative                                                                               8.48         4.64                                                 5 Invention  9.91         5.36                                                 6 Comparative                                                                               9.48         4.79                                                 7 Comparative                                                                               10.84        5.27                                                 8 Comparative                                                                               8.65         5.34                                                 9 Comparative                                                                               11.58        4.62                                                 10.sup.2 Comparative                                                                        13.17        8.63                                                 11.sup.3 Comparative                                                                        2.60         0.95                                                 ______________________________________                                                     Fiber Ratio  % Solids Barcol                                       Binder System.sup.1                                                                        PET/Glass    Pickup   Hardness                                     ______________________________________                                         1 Control   25/75        --       49.1                                         2 Comparative                                                                              25/75        1.1      50.9                                         3 Comparative                                                                              25/75        0.28     48.6                                         4 Comparative                                                                              25/75        0.15     49.4                                         5 Invention 25/75        0.20     41.7                                         6 Comparative                                                                              25/75        0.18     49.0                                         7 Comparative                                                                              25/75        0.15     47.3                                         8 Comparative                                                                              25/75        0.12     45.8                                         9 Comparative                                                                              25/75        0.15     45.5                                         10.sup.2 Comparative                                                                        0/100       --       49.4                                         11.sup.3 Comparative                                                                       0/0          --       42.2                                         ______________________________________                                                             Impact Strength                                                      Shrinkage (ft lbs/in)                                                Binder System.sup.1                                                                        (inches)    Notched  Unnotched                                     ______________________________________                                         1 Control   0.0007       9.46    13.81                                         2 Comparative                                                                              0.0006      12.85    17.01                                         3 Comparative                                                                              0.0005      11.44    15.63                                         4 Comparative                                                                              0.0003      10.59    12.55                                         5 Invention 0.0006      10.26    13.71                                         6 Comparative                                                                              0.0003      12.00    14.59                                         7 Comparative                                                                              0.0005      11.59    16.09                                         8 Comparative                                                                              0.0010       9.77    12.32                                         9 Comparative                                                                              0.0009       9.16    15.08                                         10.sup.2 Comparative                                                                       0.0005      10.84    15.13                                         11.sup.3 Comparative                                                                       0.0080       0.19     0.87                                         ______________________________________                                                      Flexural Strength                                                                           Tensile Strength                                     Binder System.sup.1                                                                         (PSI × 100)                                                                           (PSI × 100)                                    ______________________________________                                         1 Control    15.06        5.83                                                 2 Comparative                                                                               14.21        7.03                                                 3 Comparative                                                                               15.01        6.62                                                 4 Comparative                                                                               14.43        5.78                                                 5 Invention  11.56        6.26                                                 6 Comparative                                                                               13.76        6.94                                                 7 Comparative                                                                               14.21        6.68                                                 8 Comparative                                                                               14.53        6.10                                                 9 Comparative                                                                               11.88        6.03                                                 10.sup.2 Comparative                                                                        16.27        6.93                                                 11.sup.3 Comparative                                                                         2.60        0.95                                                 ______________________________________                                    

                  TABLE 8                                                          ______________________________________                                         Physical Properties of BMC Composites                                          Varying Resin Elongation                                                       ______________________________________                                         Resin                                Notched                                   Elongation,                                                                             PET/Glass Barcol    Shrinkage                                                                              Impact                                    Percent  Ratio     Hardness  in/in   ft lb/in                                  ______________________________________                                         0.9.sup.1                                                                               0/100     60.7      0.0003  8.4                                       0.9.sup.1                                                                               100/0     49.8      0.0050  14.8                                      1.8.sup.2                                                                               0/100     59.9      0.0004  7.6                                       1.8.sup.2                                                                               12.5/87.5 60.0      0.0005  7.0                                       1.8.sup.2                                                                               25/75     57.1      0.0001  7.8                                       1.8.sup.2                                                                               50/50     56.1      0.0010  12.0                                      1.8.sup.2                                                                               100/0     51.2      0.0044  14.8                                      6.1.sup.3                                                                               0/100     54.2      0.0004  8.0                                       6.1.sup.3                                                                               12.5/87.5 51.5      0.0005  9.2                                       6.1.sup.3                                                                               25/75     50.1      0.0004  9.3                                       6.1.sup.3                                                                               50/50     47.0      0.0016  11.6                                      6.1.sup.3                                                                               100/0     45.1      0.0021  16.1                                      10.sup.4 0/100     46.7      0.0003  6.6                                       10.sup.4 12.5/87.5 47.7      0.0007  8.0                                       10.sup.4 25/75     45.4      0.0006  8.4                                       10.sup.4 50/50     44.1      0.0017  11.5                                      10.sup.4 100/0     33.0      0.0032  19.6                                      ______________________________________                                         Resin     Unnotched    Flexural Tensile                                        Elongation,                                                                              Impact       Strength Strength                                       Percent   ft lb/in     psi      psi                                            ______________________________________                                         0.9.sup.1 13.3         13 000   7210                                           0.9.sup.1 24.3         4690     3140                                           1.8.sup.2 10.4         11 300   6600                                           1.8.sup.2 12.7         11 800   7050                                           1.8.sup.2 12.9         9370     5710                                           1.8.sup.2 12.9         8160     4640                                           1.8.sup.2 23.0         4960     3310                                           6.1.sup.3 10.7         14 400   8370                                           6.1.sup.3 10.9         12 500   6570                                           6.1.sup.3 16.5         9930     5670                                           6.1.sup.3 17.2         8840     5410                                           6.1.sup.3 26.6         5240     3480                                           10.sup.4   8.0         13 400   7310                                           10.sup.4  10.4         10 800   6090                                           10.sup.4  10.8         10 600   6270                                           10.sup.4  15.6         9900     4360                                           10.sup.4  26.7         3970     3100                                           ______________________________________                                    

                  TABLE 9                                                          ______________________________________                                         Physical Properties of PET/Glass                                               Fiber Reinforced Composites                                                    ______________________________________                                         PET/Glass Concentration,                                                                              Barcol   Shrinkage                                      Ratio     Percent      Hardness in/in                                          ______________________________________                                         0/100     35           46.1     0.00020                                        0/100     30           47.2     0.00039                                        0/100     25           57.3     0.00056                                        0/100     20           49.5     0.00057                                        0/100     15           52.7     0.00108                                        0/100     10           51.3     0.00123                                        50/50     35           34.2     0.00149                                        50/50     30           41.4     0.00151                                        50/50     25           46.7     0.00087                                        50/50     15           51.1     0.00155                                        25/75     35           37.3     0.00045                                        25/75     30           41.2     0.00059                                        25/75     25           48.4     0.00067                                        25/75     20           50.9     0.00064                                        25/75     15           53.1     0.00121                                        100/0     35           22.5     0.01072                                        100/0     30           29.8     0.01020                                        100/0     25           35.9     0.00937                                        100/0     20           40.1     0.00929                                        100/0     15           41.3     0.00877                                        100/0     10           46.8     0.00831                                        ______________________________________                                                 Notched   Unnotched  Flexural                                                                               Tensile                                   PET/Glass                                                                              Impact    Impact     Strength                                                                               Strength                                  Ratio   ft lb/in  ft lb/in   psi     psi                                       ______________________________________                                         0/100   16.3      20.5       17 700  6210                                      0/100   13.6      19.3       17 200  5440                                      0/100   10.0      15.4       11 100  7060                                      0/100   11.9      17.5       20 800  5850                                      0/100    8.2      14.6       15 300  5530                                      0/100    7.6      11.5       11 900  6280                                      50/50   17.3      27.7       11 000  5890                                      50/50   16.5      22.9       10 900  5380                                      50/50   14.9      19.3       13 000  4220                                      50/50   11.2      15.5       12 600  4540                                      25/75   17.0      22.8       13 800  7630                                      25/75   17.2      22.9       15 800  5830                                      25/75   14.6      18.8       13 100  6800                                      25/75   12.8      17.0       14 300  7030                                      25/75   13.5      16.0       14 200  5040                                      100/0   21.2      24.8       5960    3540                                      100/0   16.1      25.7       4550    4050                                      100/0   20.9      27.4       5790    2980                                      100/0   17.1      25.4       5810    3430                                      100/0   13.4      19.1       4780    3340                                      100/0    9.1      12.1       3640    2090                                      ______________________________________                                    

                  TABLE 10                                                         ______________________________________                                         Composite Properties                                                           System = Typical commercial polyester BMC formulation                          20 weight percent glass loading, glass replaced                                by PET on equal volume basis                                                   Fiber length = 1/2 inch                                                        ______________________________________                                                                 25% PET/   50% PET/                                                  100% Glass                                                                               75% Glass  50% Glass                                   ______________________________________                                         Physical Properties                                                            Notched impact ft lb/in                                                                      9.1       12.0       11.6                                        Tensile strength GTH                                                                         6.9       7.0        5.4                                         PSI × 10.sup.3                                                           Compressive yield                                                                            16.6      --         14.2                                        Strength psi × 10.sup.3                                                  Flexural modulus                                                                             1.9       1.5        1.2                                         psi × 10.sup.6                                                           Tensile modulus                                                                              6.3       6.0        5.1                                         psi × 10.sup.5                                                           Abrasion - 1 K cycles                                                                        3.3       2.8        2.5                                         (gr)                                                                           Acid Resistance.sup.1 (25%                                                     H.sub.2 SO.sub.4 @ 200° C.)                                             Percent tensile                                                                              28.7      --         14.4                                        strength loss                                                                  Electrical properties                                                                        189       --         192                                         arc resistance - seconds                                                       dielectric constant                                                            60 HZ         5.39      --         5.32                                        50  --MHZ     5.11      --         4.92                                        1M HZ         4.90      --         4.79                                        ______________________________________                                                               100% PET  ASTM                                           ______________________________________                                         Physical Properties                                                            Notched impact ft lb/in                                                                              16.9      D-256                                          Tensile strength GTH  3.5       D-638                                          PSI ×  10.sup.3                                                          Compressive yield     10.0      D-695                                          strength psi × 10.sup.3                                                  Flexural modulus      1.0       D-790                                          psi × 10.sup.6                                                           Tensile modulus       4.6       D-630                                          psi × 10.sup.5                                                           Abrasion - 1 K cycles 2.1       --                                             (gr)                                                                           Acid Resistance.sup.1 (25% H.sub.2 SO.sub.4 @ 200° C.)                  Percent tensile       6.5       --                                             strength loss                                                                  Electrical properties 197       D-495-73                                       arc resistance - seconds                                                       dielectric constant                                                            60 HZ                 5.13      D-150-81                                       50  --MHZ             4.81      D-150-81                                       1M HZ                 4.60      D-150-81                                       ______________________________________                                          .sup.1 Typical commercial vinyl ester BMC formulation                    

                  TABLE 11                                                         ______________________________________                                         Nylon Fiber Reinforced Composites                                                              Fiber Ratio                                                                    Nylon 6/Glass                                                                  100/0  25/75    0/100                                          ______________________________________                                         Barcol Hardness   38.4     47.3     52.5                                       Impact Notched (ft lbs/in)                                                                       12.99    9.30     8.37                                       Impact Unnotched (ft lbs/in)                                                                     17.69    9.82     12.33                                      Flex Strength (PSI × 1000)                                                                 5.38     12.28    14.60                                      Tensile Strength (PSI × 1000)                                                              2.76     5.13     5.32                                       ______________________________________                                     

What is claimed is:
 1. A fiber reinforced plastic composite comprising:a. a resin matrix; and b. a high tenacity reinforcing fiber selected from the group consisting of polyester, aliphatic polyamide, and combinations thereof, and treated with a composition consisting essentially of(i) an organofunctional silane in an amount sufficient to achieve 0.02 to 1.0 weight percent of the silane on the fiber, and (ii) a diluent which provides for the hydrolysis of the silane to a silanol; to enhance compatibility of the fiber and the resin matrix.
 2. The composite of claim 1 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
 3. The composite of claim 1 wherein the reinforcing fiber is treated with a sufficient amount of the composition to achieve 0.01 to 0.5 weight percent of the silane on the fiber.
 4. The composite of claim 1 wherein the fiber is polyester.
 5. The composite of claim 1 wherein the fiber is polyamide.
 6. The composite of claim 1 wherein the treating composition consists essentially of 1 to 50 weight percent of the silane, up to one weight percent of a wetting agent, and 49 to 99 weight percent diluent.
 7. The composite of claim 6 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
 8. The composite of claim 1 additionally comprising other reinforcing fibers.
 9. The composite of claim 8 wherein the other reinforcing fibers are glass fibers.
 10. The composite of claim 1 wherein the fiber is polyester which is treated with a sufficient amount of the composition to achieve 0.1 to 0.5 weight percent of the silane on the fiber.
 11. The composite of claim 10 wherein the treating composition consists esentially of 1 to 50 weight percent of the silane, up to 1 weight percent of a wetting agent, and 49 to 99 weight percent of the diluent.
 12. The composite of claim 11 wherein the treating composition consists essentially of 3 to 25 weight percent of the silane, up to 1 weight percent of the wetting agent, and 74 to 97 weight percent of the diluent.
 13. The composite of claim 12 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
 14. The composite of claim 13 wherein the resin matrix comprises a thermosetting resin selected from the group consisting of polyester, epoxy and vinyl ester.
 15. The composite of claim 13 wherein the resin matrix comprises an unsaturated polyester resin.
 16. The composite of claim 15 additionally comprising other reinforcing fibers.
 17. The composite of claim 16 wherein the other reinforcing fibers are glass fibers.
 18. The composite of claim 17 wherein the polyester fiber is characterized by a thermal shrinkage of up to about 11 percent, an elongation of from about 10 to 28 percent, and a modulus after cure of at least about 60 grams per denier.
 19. The composite of claim 17 wherein the polyester fiber is characterized by a tenacity of about 7 to 9 grams per denier, a thermal shrinkage of at most about 3 percent, an elongation of about 14 to 24 percent and a modulus after cure of about 70 to 90 grams per denier.
 20. The composite of claim 1 wherein the reinforcing fiber is a polyester fiber characterized by a thermal shrinkage of up to about 11 percent, an elongation of from about 10 to 28 percent and a modulus after cure of at least about 60 grams per denier.
 21. The composite of claim 1 wherein the reinforcing fiber is a polyester fiber characterized by a tenacity of about 7 to 9 grams per denier, a thermal shrinkage of at most about 3 percent, an elongation of about 14 to 24 percent and a modulus after cure of about 70 to 90 grams per denier.
 22. A high tenacity reinforcing polyamide fiber for reinforcing plastic composites, said fiber is treated with a composition consisting essentially of(i) an organofunctional silane in an amount sufficient to achieve 0.02 to 0.1 weight percent of the silane on the fiber, and (ii) a diluent which provides for the hydrolysis of the silane to a silanol;to enhance compatability of the fiber and a resin matrix.
 23. The fiber of claim 22 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
 24. The fiber of claim 22 wherein the reinforcing fiber is treated with a sufficient amount of the composition to achieve 0.01 to 0.5 weight percent of the silane on the fiber.
 25. The fiber of claim 22 wherein the treating composition consists essentially of 1 to 50 weight percent of the silane, up to one weight percent of a wetting agent, and 49 to 99 weight percent diluent.
 26. The fiber of claim 25 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
 27. The fiber of claim 22 wherein the silane is selected from the group consisting of:Vinyl-tris(beta-methoxyethoxy)silane; gamma-Methacryloxypropyltrimethoxysilane; beta(3,4-Epoxycyclohexyl)ethyltrimethoxysilane; gamma-Mercaptopropyltrimethoxysilane; gamma-Aminopropyltriethoxysilane; N-beta(aminoethyl)-gamma-aminopropyltrimethoxysilane; and ##STR3## wherein n is 2 to 5; and combinations thereof.
 28. The fiber of claim 25 wherein the silane is selected from the group consisting of:Vinyl-tris(beta-methoxyethoxy)silane; gamma-Methacryloxypropyltrimethoxysilane; beta(3,4-Epoxycyclohexyl)ethyltrimethoxysilane; gamma-Mercaptopropyltrimethoxysilane; gamma-Aminopropyltriethoxysilane; N-beta(aminoethyl)-gamma-aminopropyltrimethoxysilane; and ##STR4## wherein n is 2 to 5; and combinations thereof.
 29. The composite of claim 1 wherein the silane is selected from the group consisting of:Vinyl-tris(beta-methoxyethoxy)silane; gamma-Methacryloxypropyltrimethoxysilane; beta(3,4-Epoxycyclohexyl)ethyltrimethoxysilane; gamma-Mercaptopropyltrimethoxysilane; gamma-Aminopropyltriethoxysilane; N-beta(aminoethyl)-gamma-aminopropyltrimethoxysilane; and ##STR5## wherein n is 2 to 5; and combinations thereof.
 30. The composite of claim 6 wherein the silane is selected from the group consisting of:Vinyl-tris(beta-methoxyethoxy)silane; gamma-Methacryloxypropyltrimethoxysilane; beta(3,4-Epoxycyclohexyl)ethyltrimethoxysilane; gamma-Mercaptopropyltrimethoxysilane; gamma-Aminopropyltriethoxysilane; N-beta(aminoethyl)-gamma-aminopropyltrimethoxysilane; and ##STR6## wherein n is 2 to 5; and combination thereof.
 31. The composite of claim 12 wherein the silane is selected from the group consisting of:vinyl-tris(beta-methoxyethoxy)silane; gamma-Methacryloxypropyltrimethoxysilane; beta(3,4-Epoxycyclohexyl)ethyltrimethoxysilane; gamma-Mercaptopropyltrimethoxysilane; gamma-Aminopropyltriethoxysilane; N-beta(aminoethyl)-gamma-aminopropyltrimethoxysilane; and ##STR7## wherein n is 2 to 5; and combinations thereof. 